1、五邑大学本科毕业论文固相法及燃烧法合成Y2MoO6:Eu3+荧光粉及荧光性能研究摘要荧光粉的合成方法对其性能有很大影响,适当的合成方法可以有效的提高荧光粉的性能。传统的固相法合成的荧光粉性能优秀,不过也存在一定的不足,如:反应的温度相当的高,制备需要的时间也非常的长,能耗相对来说也不低等,在一定程度上增加了制备的成本。相对而言,燃烧法的合成温度较低,反应时间较短,在一定程度上弥补了固相法的缺点。因此,本文选取Y2MoO6为基质材料,通过掺杂Eu3+离子合成具有红色荧光的荧光粉。采用燃烧法和传统的固相法进行对比,研究了不同合成方法对其荧光性能的研究。并通过TG-DSC﹑DRX﹑SEM扫描电镜

2、﹑激发发射光谱等表征方法来对我们制备的物质的结构、形状样貌还有光谱特征做了一系列的实验探究和学习。通过对测试结果分析可知,两种方法均可制备出具有纯相的Y2MoO6:Eu3+荧光粉。通过对荧光光谱分析可知,固相法合成的样品在1000℃下具有最高的荧光发射;而燃烧法合成的样品在1100℃下表现出最好的荧光性能。关键词:结晶性;燃烧法;固相法;Y2MoO6:Eu3+;荧光性能。25五邑大学本科毕业论文Abstract The way of compounding phosphor has a major impact on its performance, which can be improv

3、ed by some proper synthetic ways. It can not be denied that traditional Solid-phase method makes the performance of phosphor excellent. However, it needs a higher compounding temperature, longer reaction time as well as higher energy consumption, which adds up the cost of production to some extent

4、. Comparativrly speaking, Combustion method has several advantages that can make up for the Solid-phase method. Such as lower compounding temperature and shorter reaction time. Thus, this passage choose  as a basic material, adding  to compound the phosphor with red fluorescent. There is a compari

5、son between the Combustion method and traditional Solid-phase method, which meets our needs to study how performance can be impacted by different synthetic ways. What’s more, we are able to study and analyze the phase structure, the shape as well as the spectral properties of the synthetic materia

6、l systematically. The characterization methods to study and analyze the phase structure  like scanning electron microscope and stimulating emission spectrum such as TG-DSC, DRX and SEM are available. Through analyzing the result of the test, it can be concluded that both of these two ways can conp

7、ound , the phosphor with . In general, the samples conpounded by the Solid-phase method have the highest flourescence emission in 1000 through analyzing flourescence spectrum while the Combustion method in 1100.K

当前文档最多预览五页,下载文档查看全文

此文档下载收益归作者所有

当前文档最多预览五页,下载文档查看全文
温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,天天文库负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。