超硬刀具材料的发展与应用分析

《超硬刀具材料的发展与应用分析》由会员上传分享，免费在线阅读，更多相关内容在应用文档-天天文库。

1、http://www.lcjcgy.com/http://www.fclqmm.com/超硬刀具材料的发展与应用分析[摘要]随着材料工业及精密机械工业的发展，精密切削、超精密切削和难切削材料使用的增多，超硬刀具材料的应用日益广泛。本文通过分析超硬刀具材料的发展状况，对主要品种的应用进行探讨。[abstract]withthedevelopmentofmaterialindustry,andprecisionmachineryindustry,precisioncutting,theultraprecisioncuttinganddifficultcuttin

2、gmaterialusedontherise,applicationofsuperhardcuttingtoolmaterialsisbecomingmoreandmorewidely.Inthispaper,byanalyzingthedevelopmentsituationofsuperhardcuttingtoolmaterial,themainvarietiesofapplicationwerediscussed.　　[关键词]超硬刀具刀具材料金刚石[keywords]diamondsuperhardcuttingtoolcuttingtoolmat

3、erials　　　　一、超硬刀具材料发展概况First,developmentgeneralsituationofsuperhardcuttingtoolmaterials　　超硬刀具材料是指天然金刚石及硬度、性能与之相近的人造金刚石和CBN(立方氮化硼)。由于天然金刚石价格比较昂贵，所以生产上大多采用人造聚晶金刚石(PCD)、聚晶立方氮化硼(PCBN)以及它们的复合材料。http://www.lcjcgy.com/http://www.fclqmm.com/Referstothenaturaldiamondsuperhardcuttingtoolmater

4、ialsandhardness,theperformancesimilartothesyntheticdiamondandCBN(cubicboronnitride).Becausenaturaldiamondpriceisexpensive,sotheproductionmostlyadoptsthesyntheticpolycrystallinediamond(PCD)andpolycrystallinecubicboronnitride(PCBN)andtheircompositematerials.　　早在20世纪50年代，美国就利用人造金刚石微粉和

5、CBN微粉在高温、高压、触媒和结合剂的作用下烧结成尺寸较大的聚晶块作为刀具材料。之后，南非戴比尔斯(DeBeem)公司、前苏联和日本也相继研制成功。20世纪70年代初又推出了金刚石或CBN和硬质合金的复合片，它们是在硬质合金基体上烧结或压制一层0.5mm～1mm的PCD或PCBN而成，从而解决了超硬刀具材料抗弯强度低、镶焊困难等问题，使超硬刀具的应用进入实用阶段。Intheearly1950s,theUnitedStateshaveusedartificialdiamondmicropowderandCBNpowderathightemperature,hi

6、ghpressure,andthecatalyticbinderburnundertheactionofbigsizeofpolycrystallineblockasthecuttingtoolmaterial.DEbeers,theSouthAfrica(DeBeem)company,theformerSovietunionandJapanhavealsosuccessfullydeveloped.Launchedintheearly1970s,thediamondorCBNandcarbidecompositefilms,theyaresinteredo

7、ncementedcarbidesubstratesorsuppressalayerof0.5mmto1mmbetweenPCDandPCBN,lowflexuralstrengthsoashttp://www.lcjcgy.com/http://www.fclqmm.com/tosolvethesuperhardcuttingtoolmaterials,weldingondifficultproblems,theapplicationofsuperhardcuttingtoolintothepracticalstage.　　我国超硬刀具材料的研究与应用开始

8、于上个世纪70年代，并于1970年在贵阳建造了我国第