熟料生产十大原则.ppt

《熟料生产十大原则.ppt》由会员上传分享，免费在线阅读，更多相关内容在PPT专区-天天文库。

1、十个基本规则熟料UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12规则一减少生料的筛余尤其是硅质筛余会降低煅烧温度、降低研磨电耗。同时会利于强度性能。关键数值？把100μm的筛余量由20%降至10%.对于细度为350m2/kg的水泥来说.每吨水泥研磨生料的总电耗会下降4kWh。UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12将节省燃

2、烧所用燃料研磨水泥的kW将生料研磨更细一点UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12CONTES更细的生料=节省燃料55.55656.55757.55858.58121620油(升/吨生料)>100µm筛余(%)UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12MARTRES生料(实验室中的)更细的生料=节省燃料油0.002.

3、004.006.008.001400145015001550160015%>100µm-实际生料5%>100µm-实验室研磨筛余5%>100µm-完全研磨%游离CaO温度°C生料UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12KARSDORF生料(实验室中的)更细的生料=节省燃料油0.002.004.006.008.0013501400145015001550160016%>100µm实际生料8%>100µm实验室重磨%游离

4、CaO温度°C生料UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12LEXOS生料y=-0.4267x+29.759202122232425121416182022kWh/t%>100µm筛余y=-0.42x+29.7r2=0.91更细的生料=生料磨电耗UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12CPAHPR(~PO52.5R)

5、LEXOS更细的生料=节省水泥磨电耗5560657075121416182022kWh/ty=1.38x+37.8r2=0.58%>100µm筛余UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12CONTES更细的生料=节省研磨水泥的kW生料纯水泥]高标号快凝水泥月份>100mm>200mm比表面积cm2/g吨/小时磨机1d2d28d二月20.02.0385049.022.535.770.0三月13.00.8385052.52

6、4.037.071.0四月-五月13.00.8368055.522.637.070.0MPaMPaMPaUpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12规则2短烧成带可提高熟料的易磨性并增加水泥的强度关键数值？窑电流在操作稳定情况下达到最小值.即优化操作。UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12易磨性与冷却带温度冷却带温度

7、45505560657075105011001150120012501300135014001450°CkWh/tBB10PortlaNouvelle烧成带愈短:熟料易磨性愈好UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12易磨性与烧成带长度(窑电流)PortlaNouvelle烧成带愈短:熟料易磨性愈好45505560657075600700800900100011001200130014001500窑传动扭矩BB10(k

8、Wh/t)NmUpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12烧成带热且短烧出易磨熟料UpdateLAFARGEDuJiangYan-ZhouXia.ZhuFang(fromHuaiBeiversion)–July03-V1.12易磨性