焊缝RT底片评判规律及典型缺陷图谱.doc

《焊缝RT底片评判规律及典型缺陷图谱.doc》由会员上传分享，免费在线阅读，更多相关内容在教育资源-天天文库。

1、焊缝射线照相底片的评判规律一、探伤人员要评片，四项指标放在先*，底片标记齐又正，铅字压缝为废片。二、评片开始第一件，先找四条熔合线，小口径管照椭圆，根部都在圈里面。三、气孔形象最明显，中心浓黑边缘浅，夹渣属于非金属，杂乱无章有棱边。四、咬边成线亦成点，似断似续常相见，这个缺陷最好定，位置就在熔合线。五、未焊透是大缺陷，典型图象成直线，间隙太小钝边厚，投影部位靠中间。六、内凹只在仰焊面，间隙太大是关键，内凹未透要分清，内凹透度成弧线。七、未熔合它斜又扁，常规透照难发现，它的位置有规律，都在坡口与层间。八、横裂纵裂都危险，横

2、裂多数在表面，纵裂分布范围广，中间稍宽两端尖。九、还有一种冷裂纹，热影响区常发现，冷裂具有延迟性，焊完两天再拍片。十、有了裂纹很危险，斩草除根保安全，裂纹不论长和短，全部都是Ⅳ级片。十一、未熔和也很危险，黑度有深亦有浅，一旦判定就是它，亦是全部Ⅳ级片。十二、危害缺陷未焊透，Ⅱ级焊缝不能有，管线根据深和长，容器跟着条渣走**。十三、夹渣评定莫着忙，分清圆形和条状，长宽相比3为界，大于3倍是条状。十四、气孔危害并不大，标准对它很宽大，长径折点套厚度，中间厚度插入法。十五、多种缺陷大会合，分门别类先评级，2类相加减去Ⅰ，3类相

3、加减Ⅱ级。十六、评片要想快又准，下拜焊工当先生，要问诀窍有哪些，焊接工艺和投影。注：*四项指标系底片的黑度、灵敏度、清晰度、灰雾度必须符合标准的要求。    **指单面焊的管线焊缝和双面焊的容器焊缝内未焊透的判定标准。RadiographInterpretation-WeldsInadditiontoproducinghighqualityradiographs,theradiographermustalsobeskilledinradiographicinterpretation.Interpretationofrad

4、iographstakesplaceinthreebasicstepswhichare..(1)detection,(2)interpretation,and(3)evaluation.Allofthesestepsmakeuseoftheradiographer'svisualacuity.Visualacuityistheabilitytoresolveaspatialpatterninanimage.Theabilityofanindividualtodetectdiscontinuitiesinradiograp

5、hyisalsoaffectedbythelightingconditionintheplaceofviewing,andtheexperiencelevelforrecognizingvariousfeaturesintheimage.Thefollowingmaterialwasdevelopedtohelpstudentsdevelopanunderstandingofthetypesofdefectsfoundinweldmentsandhowtheyappearinaradiograph.Discontinui

6、tiesDiscontinuitiesareinterruptionsinthetypicalstructureofamaterial.Theseinterruptionsmayoccurinthebasemetal,weldmaterialor"heataffected"zones.Discontinuities,whichdonotmeettherequirementsofthecodesorspecificationusedtoinvokeandcontrolaninspection,arereferredtoas

7、defects.GeneralWeldingDiscontinuitiesThefollowingdiscontinuitiesaretypicalofalltypesofwelding.Coldlapisaconditionwheretheweldfillermetaldoesnotproperlyfusewiththebasemetalorthepreviousweldpassmaterial(interpasscoldlap).Thearcdoesnotmeltthebasemetalsufficientlyand

8、causestheslightlymoltenpuddletoflowintobasematerialwithoutbonding.Porosity气孔istheresultofgasentrapmentinthesolidifyingmetal.Porositycantakemanyshapesonaradiogr