熔渣对镁碳耐火材料的腐蚀增加碳含量的影响 毕业论文外文翻译

熔渣对镁碳耐火材料的腐蚀增加碳含量的影响 毕业论文外文翻译

ID:13040338

大小:4.66 MB

页数:10页

时间:2018-07-20

熔渣对镁碳耐火材料的腐蚀增加碳含量的影响  毕业论文外文翻译_第1页
熔渣对镁碳耐火材料的腐蚀增加碳含量的影响  毕业论文外文翻译_第2页
熔渣对镁碳耐火材料的腐蚀增加碳含量的影响  毕业论文外文翻译_第3页
熔渣对镁碳耐火材料的腐蚀增加碳含量的影响  毕业论文外文翻译_第4页
熔渣对镁碳耐火材料的腐蚀增加碳含量的影响  毕业论文外文翻译_第5页
资源描述:

《熔渣对镁碳耐火材料的腐蚀增加碳含量的影响 毕业论文外文翻译》由会员上传分享,免费在线阅读,更多相关内容在学术论文-天天文库

1、熔渣对镁碳耐火材料的腐蚀增加碳含量的影响THEINFLUENCEOFCARBONCONTENTONTHECORROSIONOFMGO-CREFRACTORYMATERIALCAUSEDBYACIDANDALKALINELADLESLAGThispaperdescribesaninvestigationoftheinfluenceofincreasingcarboncontentonthecorrosionofMgO-Crefractorymaterialbymoltenslag.Therefractorymaterialcontainedmassfractionof98%MgO,

2、approximately2%Fe2O3,andgradedquantitiesfrom3%to18%C.Thecorrosionwasinvestigatedinmeltsofreductionladleslagsatatemperatureof1600°Cinlaboratoryconditions.Asampleofrefractorymaterialwithdimensionsof10×10×100mmwassubmergedintothemoltenslagandexposedtothecorrosiveeffectoftheslagfor60min.Afterthee

3、xposeoftherefractorymaterialtheslagwascooleddownandsubmittedtoachemicalanalysis.AfteracomparisonoftheMgOcontentintheslagbeforeandafterthecorrosiontesttheamountofMgOcontentinthemeltwasdeterminedandthedegreeofcorrosionoftherefractorymaterialwasquantified.Theexperimentswererealisedusingfinalslag

4、sfromtheladlefurnace(LF),stronglyalkalineslagw(CaO)/w(SiO2)=4.43,andalsoacidicslagsw(CaO)/w(SiO2)=0.94withdifferentcontentsofCaF2.TheworkwascarriedoutwithintheframeoftheprojectsEUREKAE!3580andIMPULSFI-IM4/110.RESULTSThechemicalcompositionoftheslagsbeforetheexposureisgivenintheTable1.Table1sho

5、wsthattheacidicslagcontainsverylittleoftheCaF2(w=0.82%),andthatthealkalineslagcontains7.18%CaF2,addedtoincreaseitsfluidity.Table1:ChemicalcompositionandalkalinityoftheslagsusedforthecorrosiontestTabela1:Kemi~nasestavainbazi~nost`linder,kistabiliuporabljenizapreizkusekorozijeTheMgOcontentofthe

6、slagsafterexposuretotherefractorymaterialisshowninTables2and3.ThetablesalsocontainincrementsoftheMgOcontentandtheincrementsrelatedtotheinitialMgOcontentintheslags(MgO).Thesixtestedsamplesofrefractorymaterialdifferedonlyintermsofthecarboncontent,gradedfrom3%to18%.However,sample5%contained15%Ci

7、nadditiontoanantioxidant.Table2:ChangestotheMgOcontentinanacidicslagfordifferentcarboncontentsintherefractorymaterialTabela2:SpremembevsebnostiMgOvkisli`lindriprirazli~nivsebnostiogljikavognjevzdr`nemmaterialuTable3:ChangestotheMgOcontentsina

当前文档最多预览五页,下载文档查看全文

此文档下载收益归作者所有

当前文档最多预览五页,下载文档查看全文
温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,天天文库负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。